SikaWrap® Hex-103 C
SikaWrap® Hex-103 C is a high strength, unidirectional carbon fiber fabric pre-saturated to form a carbon fiber reinforced polymer (CFRP) used to strengthen structural concrete elements.
- Used for shear, confinement or flexural strengthening
- Flexible, can be wrapped around complex geometries
- High Strength
- Light Weight
- Non-corrosive
- Alkali Resistant
- Low aesthetic impact
Usage
Load Increases- Increased live loads
- Increased traffic volumes on bridges
- Installation of heavy machinery in industrial buildings
- Vibrating structures
- Changes of building utilization
- Column wrapping
- Masonry walls
- Aging of construction materials
- Vehicle impact
- Fire
- Blast resistance
- Removal of walls or columns
- Removal of slab sections for openings
- Insufficient reinforcements
- Insufficient structural depth
Advantages
- Used for shear, confinement or flexural strengthening
- Flexible, can be wrapped around complex geometries
- High Strength
- Light Weight
- Non-corrosive
- Alkali Resistant
- Low aesthetic impact
Packaging
Rolls: 25 in. x 50 ft.; 25" x 300 ft.
Product Details
APPROVALS / CERTIFICATES
- Approved by ICC ESR-3288
- IBC 2015 Compliance
Fibre type
0° (unidirectional)
Shelf life
10 years in original packaging
Storage conditions
Store dry at 40–95 °F (4–35 °C)
Dry fibre thickness
0.0135 in. (0.34 mm)
Mass per area
18 oz. / sq. yd. (611 g/m2)
Dry fibre tensile strength
550 ksi (3,793 MPa)
Dry fibre modulus of elasticity in tension
34 msi (234.5 GPa)
Dry fibre elongation at break
1.5%
Design nominal thickness
0.04 in. (1.0 mm)
Laminate tensile strength
Average Ultimate Value | Design Value |
181.0 ksi (1,248 MPa) | (f*fu) 160.9 ksi (1,110 MPa)* |
* Average ultimate value minus 3 standard deviations
Average Ultimate Value | Design Value |
- | 6.4 kips/in./ply |
Laminate modulus of elasticity in tension
Average Ultimate Value | Design Value |
- | (ET) 10.39 msi (71.7 GPa) |
* Average ultimate value minus 3 standard deviations
Laminate elongation at break in tension
|
Tensile stiffness
Average Ultimate Value | Design Value |
- | (Ef*A) 416 kips/in. width |
* Average ultimate value minus 3 standard deviations
Application
SUBSTRATE PREPARATION
Surface must be clean and sound. It may be dry or damp, but free of standing water and frost. Remove dust, laitance, grease, curing compounds, impregnations, waxes, foreign particles, disintegrated materials and other bond inhibiting materials from the surface. Consult the current product data sheets for Sikadur® 340 for additional information on surface preparation.
Existing uneven surfaces must be filled with an appropriate repair mortar. The adhesive strength of the concrete must be verified after surface preparation by random pull-off test- ing (ASTM D-4541) at the discretion of the engineer. Minimum tensile strength, 200 psi (1.4 MPa) with concrete substrate failure.
Preparation Work: Concrete - Blast clean, shotblast or use other approved mechanical means to provide a roughened, open-textured surface. Round all corners to 1/2” radius in certain “contact critical” applications and at the engineers discretion, a thorough cleaning of the substrate using low pressure sand or water blasting may be sufficient.