SikaGrout®-214 MY
SikaGrout®-214 MY is a dual-shrinkage compensated self-levelling, premixed cementitious grout with extended working time to suit local ambient temperatures.
- Easy to mix and apply
- Good flow characteristics
- Rapid strength development
Usage
SikaGrout®-214 MY is suitable for the following grouting works with clearance of 10 mm or more:- Machine foundations
- Columns in precast constructions
- Concrete anchors
- Bridge bearings
- Cavities
- Gaps
- Recesses
- Rail beds
Advantages
SikaGrout®-214 MY is an economical and easy to use material requiring the simple addition of water. Other beneficial properties are:- Easy to mix and apply
- Good flow characteristics
- Rapid strength development
- High ultimate strength
- Impact resistant
- Non-corrosive
- Non-toxic
- Iron and chloride free
- Dense and non-shrink (2-step expansion)
- Extended working time
Packaging
25 kg bag
Colour
Grey premixed powder
Product Details
Shelf life
6 months from the date of production
Storage conditions
Store properly in original, unopened and undamaged sealed packaging in dry conditions between +10 °C to +35 °C. Protect from direct sunlight, rain and water.
Maximum Grain Size
3.3 mm
Compressive Strength
Flowable consistency
| 24 hours | > 20 N/mm² |
| 7 days | > 50 N/mm² |
| 28 days | > 60 N/mm² |
Expansion
At 24 hours
| Flowable consistency | Pourable consistency | Stiff consistency |
| 0.70 % | 0.30 % | 0.07 % |
Reaction to Fire
| Class A1 | (EN 13501-1) |
Application
Mixing Ratio
| Consistency | Water per 25 kg of grout |
| Flowable | 4.0–4.4 L |
| Pourable | 3.6–4.0 L |
| Stiff | 3.0–3.4 for special application such as anchoring starter bars |
Fresh Mortar Density
~2.2 kg/l (depending on consistency and temperature)
Layer Thickness
100 mm max. per pour / 10 mm min. per pour
Flowability
| Flowable consistency | Pourable consistency | Stiff consistency |
| 300 mm | 270 mm | 180 mm* |
* after 15 strokes
Ambient Air Temperature
+10 °C min. / +40 °C max.
Substrate Temperature
+10 °C min. / +40 °C max.
Setting Time
| Flowable consistency | Pourable consistency | Stiff consistency |
| 4 h : 30 m | 3 h : 40 m | 3 h : 00 m |
Yield
Flowable consistency
| SikaGrout®-214 MY | 1.8 kg | 25 kg | 72 x 25 kg |
| Water | 0.3 L | 4.2 L | 302 L |
| Volume mortar | 1 L | 13.9 L | 1 m³ |
Pourable consistency
| SikaGrout®-214 MY | 1.9 kg | 25 kg | 76 x 25 kg |
| Water | 0.3 L | 4 L | 303 L |
| Volume mortar | 1 L | 13.2 L | 1 m³ |
MIXING
Place 70–80 % of the premeasured clean water (depending on consistency required – refer to “Mix Ratio”) into a clean container and gradually add the whole bag of SikaGrout®-214 MY into it while continuously mixing. Add the remaining water until the desired consistency is obtained.
Mix for 2 – 3 minutes with a low speed drill (500 rpm max.).
APPLICATION
Use SikaGrout®-214 MY for grouting only.
After mixing, stir lightly with a spatula for a few seconds to release any entrapped air. The grout is then poured immediately into the prepared formwork.
When carrying out baseplate grouting, ensure sufficient pressure head it maintained for uninterrupted mortar flow. For formwork repair, the prepared formwork must be firmly in place and kept watertight.
When placing grout over a large area, it is important to maintain a continuous flow throughout. Work sequence must be properly organised to ensure an uninterrupted flow.
For sections thicker than 100 mm or for grouting large areas, it is necessary to mix SikaGrout®-214 MY with graded 10 mm silt free aggregates to minimise temperature rise generated during curing stage. The quantity of aggregates should not exceed 1 part aggregates to 1 part SikaGrout®-214 MY by weight. Other precautions such as the use of chilled water, insulation of the formwork or baseplate may be required. Please consult our Technical Service Department for assistance.
To further ensure that air entrapped during mixing is allowed to fully escape, it may be necessary to make breather holes. Use steel rods or chains to assist the flow of grout where necessary.
CLEANING OF EQUIPMENT
Clean all tools and application equipment with water immediately after use. Hardened or cured material can only be mechanically removed.